ASME B16.5 A182 F316L Welding Neck Flange Raised Face 8 Inch S/80S 600#
Short Description
Model No.: F316L-Welding-Neck-Flange-Raised-Face-8-Inch-S/80S-600#
China Welding Neck Flange Manufacturer www.ugsteelmill.com offers ASME B16.5 A182 F316L Welding Neck Flange Raised Face, 8 Inch, S/80S, 600#.
Key Specifications / Features
Type: 316L Welding Neck Flange
Material: A182 F316L
Pressure: 600#
Size: DN200 (8″)
Standard: ASME B16.5
Ends: Raised Face
Chemical Composition and Mechanical Property for 316L |
|||||||||||
Steel Grade |
Chemical Composition |
Mechanical Performance |
|||||||||
C(Max) |
Si(Max) |
Mn(Max) |
P(Max) |
S(Max) |
Ni |
Cr |
N(Max) |
Mo |
Tensile Strength |
Yield Strength |
|
Mpa |
Mpa |
||||||||||
316L |
0.03 |
0.75 |
2.00 |
0.045 |
0.03 |
10.0–14.0 |
16.0–18.0 |
0.1 |
2.00–3.00 |
485 |
170 |
ANSI/ASME/ASA B16.5 600lb/sq.in. WELDING NECK FLANGE RF | |||||||||||
ø | D | b | g | m | a | J* | h | k | Holes | l | Kg. |
1/2″ | 95,2 | 14,3 | 34,9 | 38,1 | 21,3 | 15,7 | 52,4 | 66,7 | 4 | 15,9 | 0,900 |
3/4″ | 117,5 | 15,9 | 42,9 | 47,6 | 26,7 | 20,9 | 57,1 | 82,5 | 4 | 19,0 | 1,500 |
1″ | 123,8 | 17,5 | 50,8 | 54,0 | 33,5 | 26,7 | 61,9 | 88,9 | 4 | 19,0 | 1,900 |
1 1/4″ | 133,3 | 20,6 | 63,5 | 63,5 | 42,2 | 35,0 | 66,7 | 98,4 | 4 | 19,0 | 2,600 |
1 1/2″ | 155,6 | 22,2 | 73,0 | 69,8 | 48,3 | 40,9 | 69,8 | 114,3 | 4 | 22,2 | 3,300 |
2″ | 165,1 | 25,4 | 92,1 | 84,1 | 60,3 | 52,6 | 73,0 | 127,0 | 8 | 19,0 | 4,700 |
2 1/2″ | 190,5 | 28,6 | 104,8 | 100,0 | 73,1 | 62,7 | 79,4 | 149,2 | 8 | 22,2 | 6,500 |
3″ | 209,5 | 31,7 | 127,0 | 117,5 | 88,9 | 78,0 | 82,5 | 168,3 | 8 | 22,2 | 8,700 |
3 1/2″ | 228,6 | 34,9 | 139,7 | 133,3 | 101,6 | 90,1 | 85,7 | 184,1 | 8 | 25,4 | 11,200 |
4″ | 273,0 | 38,1 | 157,2 | 152,4 | 114,3 | 102,4 | 101,6 | 215,9 | 8 | 25,4 | 18,100 |
5″ | 330,2 | 44,4 | 185,7 | 188,9 | 141,2 | 128,2 | 114,3 | 266,7 | 8 | 28,6 | 30,500 |
6″ | 355,6 | 47,6 | 215,9 | 222,2 | 168,4 | 154,2 | 117,5 | 292,1 | 12 | 28,6 | 36,200 |
8″ | 419,1 | 55,6 | 269,9 | 273,0 | 219,1 | 202,7 | 133,3 | 349,2 | 12 | 31,7 | 56,500 |
10″ | 508,0 | 63,5 | 323,8 | 342,9 | 273,0 | 254,5 | 152,4 | 431,8 | 16 | 34,9 | 91,000 |
12″ | 558,8 | 66,7 | 381,0 | 400,0 | 323,8 | 304,8 | 155,6 | 488,9 | 20 | 34,9 | 105,000 |
14″ | 603,2 | 69,8 | 412,7 | 431,8 | 355,6 | * | 165,1 | 527,0 | 20 | 38,1 | 125,000 |
16″ | 685,8 | 76,2 | 469,9 | 495,3 | 406,4 | 177,8 | 603,2 | 20 | 41,3 | 178,000 | |
18″ | 742,9 | 82,5 | 533,4 | 546,1 | 457,2 | 184,1 | 654,0 | 20 | 44,4 | 261,000 | |
20″ | 812,8 | 88,9 | 584,2 | 609,6 | 508,0 | 190,5 | 723,9 | 24 | 44,4 | 268,000 | |
22″ | 869,9 | 95,2 | 641,2 | 666,7 | 558,8 | 196,8 | 777,9 | 24 | 47,6 | 328,000 | |
24″ | 939,8 | 101,6 | 692,1 | 717,5 | 609,6 | 203,2 | 838,2 | 24 | 50,8 | 380,000 | |
* | The data “J” corresponds to the STD schedule | ||||||||||
To be specifiedby customer |
NOTE:
1. Class 600 flanges except Lap Joint will be furnished with 0.25 (6.35mm) raised face, which is not included in ‘Thickness’ (C) and ‘Length through Hub’ (Y1), (Y3). 2. For Slip-on, Threaded, Socket Welding and Lap Joint Flanges, the hubs can be shaped either vertical from base to top or tapered within the limits of 7 degrees. 3. Blind Flanges may be made with the same hub as that used for Slip-on Flanges or without hub. 4. The gasket surface and backside (bearing surface for bolting) are made parallel within 1 degree. To accomplish parallelism, spot facing is carried out according to MSS SP-9, without reducing thickness (C). 5. Dimensions of sizes 1/2 through 3 1/2 are the same as for Class 400 Flanges. 6. Depth of Socket (D) is covered by ANSI B 16.5 only in sizes through 3 inch, over 3 inch is at the manufacturer’s option. 7. Welding Neck Flange Bore Size SCH10, SCH20, SCH30, STD, SCH40, SCH60, SCH80, SCH100, SCH 120, SCH140, SCH160, XS |
PT – PENETRATION TESTING
This method is used for detection of welding discontinuities (material discontinuities) appearing on the surface of a welded connector. This test is done following a visual testing of a welded connector and used mainly for both ferromagnetic and non-ferromagnetic materials.